Optical properties of Silicon (Si)

Si - Silicon

Optical properties

    Remarks Referens
Dielectric constant (static) 11.7 300 K  
Infrared refractive index n(λ)   n = 3.42 300K  
    n = 3.38(1 + 3.9·10-5·T) 77K < T < 400 K  
Radiative recombination coefficient   1.1 x 10-14 cm3 s-1 300 K  
Optical photon energy   63 meV 300 K  
Absorption coefficient   αn = 10-18·no·λ2 300 K , λ ≥ 5µm, Schroeder et al. (1978)

Refractive index n versus photon energy.
T = 300 K. (Philipp and Taft [1960]).
Experimental (dashed line) and theoretical (solid line) values of reflectance versus photon energy for Si.
(Chelikowsky and Cohen [1976]).
Low-level absorption spectrum of high purity Si at various temperatures.
(Macfarlane et al. [1959]).
Intrinsic absorption edge at different doping levels.
T = 300 K. (Woltson and Subashiev [1967]).

A ground state Rydberg energy Ro = 14.7 meV.

Intrinsic absorption edge at different doping levels.
T = 300 K. (Woltson and Subashiev [1967]).
The absorption coefficient vs. photon energy at different temperatures.
1. and 2. - (Sze [1981]);
3. - (Jellison and Modine [1982]).
Free carrier absorption vs. wavelength at different doping levels (n-Si). 300 K.
Conduction electron concentrations are:
1 -- 1.4·1016 cm-3,
2 -- 8·1016 cm-3,
3 -- 1.7·1017 cm-3,
4 -- 3.2·1017 cm-3,
5 -- 6.1·1018 cm-3,
6 -- 1·1019 cm-3.
Spitzer & Fan (1957)
At 300 K for λ ≥ 5µm,
αn = 10-18·no·λ2
(Schroeder et al. [1978]).
Free carrier absorption vs. wavelength at different doping levels (p-Si). 300 K.
Hole concentrations are
1 -- 4.6·1017 cm-3;
2 -- 1.4·1018 cm-3;
3 -- 2.5·1018 cm-3;
4 -- 1.68·1019cm-3.
Hara & Nishi (1966)
At 300 K for λ ≥ 5µm,
αp≈ 2.7·10-18·po·λ2
(Schroeder et al. [1978]).
Free carrier absorption versus wavelength for high purity Si at different temperatures.
Temperatures are 1. 300 K; 2. 473 K; 3. 573 K; 4. 623 K; 5. 673 K.
(Runyan [1966]).
Free carrier absorption versus wavelength for high purity Si at different temperatures.
Temperatures are 1. 300 K; 2. 473 K; 3. 573 K; 4. 623 K; 5. 673 K.
(Runyan [1966]).